Roll-off reducing agent

ABSTRACT

A roll-off reducing agent comprising one or more compounds selected from the group consisting of carboxylic acids having 2 to 20 carbon atoms having either OH group or groups or SH group or groups, monocarboxylic acids having 1 to 20 carbon atoms, and dicarboxylic acids having 2 to 3 carbon atoms, and salts thereof; and a roll-off reducing agent composition comprising a roll off-reducing agent comprising one or more compounds selected from the group consisting of carboxylic acids having 2 to 20 carbon atoms having either OH group or groups or SH group or groups, monocarboxylic acids having 1 to 20 carbon atoms, and dicarboxylic acids having 2 to 3 carbon atoms, and salts thereof; an abrasive; and water.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a roll-off reducing agent. Morespecifically, the present invention relates to a roll-off reducing agentcomposition comprising the roll-off reducing agent, a process ofreducing roll-off of a polished substrate by applying the roll-offreducing agent to the substrate, a process for producing a polishedsubstrate by applying the roll-off reducing agent to the substrate, apolishing composition, a polishing process of a substrate to be polishedby applying the polishing composition to the substrate, and a processfor producing a substrate by applying the polishing composition to asubstrate to be polished.

2. Discussion of the Related Art

Over the years, a demand for a technique for further increasing thecapacity of the hard discs has become greater. As a leading means forincreasing the capacity of the hard discs, there has been considered ameans of producing a substrate capable of recording data even to itsouter periphery by reducing roll-off (edge rounding of end side of asubstrate) caused in the polishing process. For instance, variousmechanical polishing conditions which can reduce roll-off, such asmaking a polishing pad more rigid, and making a polishing load smaller,have been studied. However, although a certain extent of an effect isobtained for reducing roll-off by these mechanical polishing conditions,the effect has not yet been satisfactory.

In addition, as a polishing composition capable of reducing roll-off, acomposition comprising water, α-alumina particles and aluminum nitratehas been known (Japanese Patent Laid-Open No. Hei 9-286975). However,this composition does not have a satisfactory effect of reducingroll-off, and studies of the polishing components having an excellenteffect for reducing roll-off have not yet been sufficiently made atpresent.

On the other hand, the hard discs have been greatly developed over theyears in the trends of miniaturization and high capacity, so that thetrend of high density has been progressed, that the minimum recordingarea has become smaller, and that the floating amount of a magnetic headhas been made increasingly smaller. Therefore, there have been desiredto increase the polishing rate and reduce the surface roughness, and toreduce surface defects such as scratches and pits in the polishingprocess of a hard disc substrate. In view of this, there have beenstudied on a polishing composition by using water, alumina, boehmite anda chelating compound (Japanese Patent Laid-Open No. Hei 11-92749, andthe like); a polishing composition comprising water, α-alumina, and analumina sol stabilized with acetic acid (Japanese Patent Laid-Open No.2000-63805); a polishing composition for an aluminum magnetic disc,comprising water, an alumina abrasive powder, a polishing acceleratorsuch as gluconic acid or lactic acid, and a surface-modifying agent suchas a colloidal alumina (Japanese Patent Laid-Open No. Hei 2-84485); apolishing composition comprising water, an alumina abrasive, and apolishing accelerator comprising molybdic acid and an organic acid(Japanese Patent Laid-Open No. Hei 7-216345); and a polishing process.

However, none of these polishing compositions sufficiently satisfy allof an effect of reducing roll-off, an effect of increasing the polishingrate, an effect of reducing the surface roughness of a polished object,and an effect of reducing surface defects such as scratches and pits.Therefore, a polishing composition having further enhanced effects is indemand.

An object of the present invention is to provide a roll-off reducingagent capable of reducing roll-off of a polished substrate caused bypolishing, and increasing a polishing rate; a roll-off reducing agentcomposition comprising the roll-off reducing agent; a process ofreducing roll-off of a polished substrate by using the roll-off reducingagent; and a process for producing a polished substrate by using theroll-off reducing agent.

Also, another object of the present invention is to provide a polishingcomposition having an increased polishing rate, and a reduced surfaceroughness without causing a surface defect on the surface of thepolished substrate, and being capable of reducing roll-off; a polishingprocess of a polished substrate by using the polishing composition; anda process for producing a polished substrate.

These and other objects of the present invention will be apparent fromthe following description.

In the present specification, the term “roll-off” refers to a stateso-called edge rounding of an end surface, in which a part of an endsurface of a substrate to be polished is more largely grinded ascompared to that of the central part, thereby rounding off the end part.

SUMMARY OF THE INVENTION

According to the present invention, there are provided:

-   [1] a roll-off reducing agent comprising one or more compounds    selected from the group consisting of carboxylic acids having 2 to    20 carbon atoms having either OH group or groups or SH group or    groups, monocarboxylic acids having 1 to 20 carbon atoms, and    dicarboxylic acids having 2 to 3 carbon atoms, and salts thereof;-   [2] a roll-off reducing agent composition comprising:    -   a roll-off reducing agent comprising one or more compounds        selected from the group consisting of carboxylic acids having 2        to 20 carbon atoms having either OH group or groups or SH group        or groups, monocarboxylic acids having 1 to 20 carbon atoms, and        dicarboxylic acids having 2 to 3 carbon atoms, and salts        thereof;    -   an abrasive; and    -   water;-   [3] a polishing composition comprising:    -   water;    -   an abrasive;    -   a roll-off reducing agent comprising one or more compounds        selected from the group consisting of carboxylic acids having 2        to 20 carbon atoms having either OH group or groups or SH group        or groups, monocarboxylic acids having 1 to 20 carbon atoms, and        dicarboxylic acids having 2 to 3 carbon atoms, and salts        thereof; and    -   an intermediate alumina;-   [4] a polishing composition comprising:    -   (A) one or more compounds selected from carboxylic acids having        2 to 20 carbon atoms having either OH group or groups or SH        group or groups, monocarboxylic acids having 1 to 20 carbon        atoms, and dicarboxylic acids having 2 to 3 carbon atoms, and        salts thereof;    -   (B) one or more compounds selected from polycarboxylic acids        having 4 or more carbon atoms and having neither OH group or        groups nor SH group or groups, aminopolycarboxylic acids, amino        acids and salts thereof; and    -   (C) one or more compounds selected from an intermediate alumina        and an alumina sol;    -   an abrasive; and    -   water;-   [5] a polishing composition comprising:    -   (A) one or more compounds selected from carboxylic acids having        2 to 20 carbon atoms having either OH group or groups or SH        group or groups, monocarboxylic acids having 1 to 20 carbon        atoms, and dicarboxylic acids having 2 to 3 carbon atoms, and        salts thereof; and

(B) one or more compounds selected from polycarboxylic acids having 4 ormore carbon atoms and having neither OH group or groups nor SH group orgroups, aminopolyearboxylic acids, amino acids and salts thereof;

-   -   an abrasive; and    -   water;

-   [6] a process of reducing roll-off of a polished substrate,    comprising applying to a substrate to be polished a roll-off    reducing agent comprising one or more compounds selected from the    group consisting of carboxylic acids having 2 to 20 carbon atoms    having either OH group or groups or SH group or groups,    monocarboxylic acids having 1 to 20 carbon atoms, and dicarboxylic    acids having 2 to 3 carbon atoms, and salts thereof;

-   [7] a process for producing a polished substrate, comprising a step    of applying to a substrate to be polished a roll-off reducing agent    comprising one or more compounds selected from the group consisting    of carboxylic acids having 2 to 20 carbon atoms having either OH    group or groups or SH group or groups, monocarboxylic acids having 1    to 20 carbon atoms, and dicarboxylic acids having 2 to 3 carbon    atoms, and salts thereof;

-   [8] a polishing process of a substrate to be polished comprising a    step of polishing the substrate to be polished with the polishing    composition of any one of items [3] to [5] above; and

-   [9] a process for producing a substrate comprising a step of    polishing a substrate to be polished with the polishing composition    of any one of items [3] to [5] above.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a graph showing a roll-off in connection with the detectioncurve.

DETAILED DESCRIPTION OF THE INVENTION

1. Roll-off Reducing Agent

The roll-off reducing agent used in the present invention is one or morecompounds selected from the group consisting of carboxylic acids having2 to 20 carbon atoms having either OH group or groups or SH group orgroups, monocarboxylic acids having 1 to 20 carbon atoms, anddicarboxylic acids having 2 to 3 carbon atoms, and salts thereof. Amongthem, the carboxylic acids having 2 to 20 carbon atoms having either OHgroup or groups or SH group or groups, the dicarboxylic acids having 2to 3 carbon atoms, and salts thereof are preferable, from the viewpointof an effect of improving roll-off.

The carboxylic acid having 2 to 20 carbon atoms having either OH groupor groups or SH group or groups includes oxycarboxylic acids, andcompounds in which an oxygen atom of the OH group of the oxycarboxylicacid is substituted by a sulfur atom. It is desired that the number ofcarbon atoms of these carboxylic acids is from 2 to 20, preferably from2 to 12, more preferably from 2 to 8, still more preferably from 2 to 6,from the viewpoint of the solubility to water. In addition, asoxycarboxylic acids, those having a hydroxyl group at α-position of acarboxyl group are preferable, from the viewpoint of reducing roll-off.

It is desired that the number of carbon atoms of the monocarboxylic acidis from 1 to 20, preferably from I to 12, more preferably from 1 to 8,still more preferably from 1 to 6, from the viewpoint of the solubilityto water.

The dicarboxylic acid is those having 2 to 3 carbon atoms, namely oxalicacid and malonic acid, from the viewpoint of reducing roll-off. Amongthese roll-off reducing agents, the oxycarboxylic acids are preferable,from the viewpoint of increasing the polishing rate. In addition, thedicarboxylic acids are preferable, from the viewpoint of reducingroll-off.

Concrete examples of the carboxylic acid having 2 to 20 carbon atomshaving either OH group or groups or SH group or groups include glycolicacid, mercaptosuccinic acid, thioglycolic acid, lactic acid,β-hydroxypropionic acid, malic acid, tartaric acid, citric acid,isocitric acid, allocitric acid, gluconic acid, glyoxylic acid, glycericacid, mandelic acid, tropic acid, benzilic acid, salicylic acid, and thelike. Concrete examples of the monocarboxylic acid include formic acid,acetic acid, propionic acid, butyric acid, isobutyric acid, valericacid, isovaleric acid, hexanoic acid, heptanoic acid, 2-methylhexanoicacid, octanoic acid, 2-ethylhexanoic acid, nonanoic acid, decanoic acid,lauric acid, and the like. Among them, acetic acid, oxalic acid, malonicacid, glycolic acid, lactic acid, malic acid, tartaric acid, glyoxylicacid, citric acid and gluconic acid are preferable; oxalic acid, malonicacid, glycolic acid, lactic acid, malic acid, tartaric acid, glyoxylicacid, citric acid and gluconic acid are more preferable; and oxalicacid, malonic acid, glycolic acid, tartaric acid and glyoxylic acid areespecially preferable.

In addition, when oxalic acid, malic acid, tartaric acid, citric acid orgluconic acid is used alone or in combination with other roll-offreducing agent, it is preferable because clogging of the abrasive grainsand polishing grounds in the polishing pad can be reduced, so that thedeterioration of the polishing properties such as polishing rate andsurface qualities by using the polishing pad for a long period of timecan be prevented. Also, a frequent pad washing would not be necessary,namely the distance between the pad dressings can be remarkablyextended, so that the productivity is increased, thereby making itpreferable also from the viewpoint of economic advantages. Among them,oxalic acid, tartaric acid and citric acid are preferable, andespecially citric acid is preferable. Each of the monocarboxylic acidand the dicarboxylic acid used in the present invention is selected fromcarboxylic acids having neither OH group or groups nor SH group orgroups.

The salts of these acids (namely, carboxylic acids having 2 to 20 carbonatoms having either OH group or groups or SH group or groups,monocarboxylic acids having 1 to 20 carbon atoms, and dicarboxylic acidshaving 2 to 3 carbon atoms) are not particularly limited. Concretely,there are included salts with a metal, ammonium, an alkylammonium, anorganic amine, and the like. Concrete examples of the metal includemetals belonging to Group 1A, 1B, 2A, 2B, 3A, 3B, 4A, 6A, 7A or 8 of thePeriodic Table (long period form). Among these metals, from theviewpoint of reducing roll-off, those metals belonging to Group 1A, 3A,3B, 7A or 8 of the Periodic Table are preferable, and those metalsbelonging to Group 1A, 3A or 3B of the Periodic Table are morepreferable. Sodium and potassium belonging to Group 1A are mostpreferable.

Concrete examples of the alkylammonium include tetramethylammonium,tetraethylammonium, tetrabutylammonium, and the like.

Concrete examples of the organic amine include dimethylamine,trimethylamine, alkanolamines, and the like.

Among these salts, ammonium salts, sodium salts and potassium salts areespecially preferable.

2. Roll-off Reducing Agent Composition

The roll-off reducing agent of the present invention can be used byformulating the agent in a polishing liquid comprising an abrasive andwater. The polishing composition obtained above is especially referredto “roll-off reducing agent composition” in the present specification.Specifically, the roll-off reducing agent composition of the presentinvention comprises the above-mentioned roll-off reducing agent, anabrasive and water.

The content of the roll-off reducing agent in the roll-off reducingagent composition is preferably 0.01% by weight or more, from theviewpoints of reducing roll-off and increasing the polishing rate, andthe content of the roll-off reducing agent is preferably 5% by weight orless, from the viewpoints of economic advantages and improving surfacequalities. The content of the roll-off reducing agent is more preferablyfrom 0.01 to 3% by weight, still more preferably from 0.01 to 2% byweight, most preferably from 0.02 to 1% by weight. Here, the roll-offreducing agent can be used alone or in admixture of two or more kinds.

As the abrasive used in the present invention, any abrasives generallyemployed for polishing can be used. The abrasive includes, for instance,metals; carbides of metals or metalloids, nitrides of metals ormetalloids, oxides of metals or metalloids, borides of metals ormetalloids, diamond, and the like. The metals or metalloids includethose elements belonging to the Groups 2A, 2B, 3A, 3B, 4A, 4B, 5A, 6A,7A or 8 of the Periodic Table (long period form). Concrete examples ofthe abrasive include α-alumina particles, silicon carbide particles,diamond particles, magnesium oxide particles, zinc oxide particles,cerium oxide particles, zirconium oxide particles, colloidal silicaparticles, filmed silica particles, and the like. It is preferable touse these abrasives in admixture of two or more kinds, from theviewpoint of increasing the polishing rate. Among them, α-aluminaparticles, cerium oxide particles, zirconium oxide particles, colloidalsilica particles, fumed silica particles, and the like are morepreferable, and α-alumina particles are especially preferable.

The average primary particle size of the abrasive is preferably from0.01 to 3 μm, more preferably from 0.02 to 0.8 μm, especially preferablyfrom 0.05 to 0.5 μm, from the viewpoint of increasing the polishingrate. Further, when the primary particles are aggregated to form asecondary particle, the average secondary particle size is preferablyfrom 0.05 to 3 μm, more preferably from 0.1 to 1.5 μm, especiallypreferably from 0.2 to 1.2 μm, from the viewpoint of increasing thepolishing rate in the same manner as above, and from the viewpoint ofreducing the surface roughness of a polished object. The average primaryparticle size of the abrasive is obtained by subjecting the abrasive toan image analysis by observing with a scanning electron microscope(favorably from 3000 to 30000 times), and determining the particle sizeas a number-average particle size. In addition, the average secondaryparticle size can be determined as volume-average particle size by usinga laser diffraction method.

The specific gravity of the abrasive is preferably from 2 to 6, morepreferably from 2 to 5, from the viewpoints of the dispersibility, thefeed ability to the polishing device and recovery and reuse.

The content of the abrasive is preferably from 1 to 40% by weight, morepreferably from 2 to 30% by weight, still more preferably from 3 to 15%by weight, of the roll-off reducing agent composition, from theviewpoints of having economic advantages and making the surfaceroughness of a polished object small, thereby efficiently polishing thesubstrate.

Water in the roll-off reducing agent composition of the presentinvention is used as a medium, and the content of water is preferablyfrom 50 to 98.99% by weight, more preferably 60 to 98% by weight, stillmore preferably from 70 to 95% by weight, from the viewpoint ofefficiently polishing the object to be polished.

In addition, the roll-off reducing agent composition of the presentinvention can contain other components as occasion demands.

As other components, there are included organic acids and salts otherthan those listed as the roll-off reducing agent. The other componentsinclude, for instance, organic acids such as polycarboxylic acids,aminopolycarboxylic acids and amino acids, and salts thereof, inorganicacids and salts thereof, oxidizing agents, thickeners, dispersants,anticorrosive agents, basic substances, surfactants, and the like.Concrete examples of the organic acids and salts thereof, inorganicacids and salts thereof, and the oxidizing agents are those listed inJapanese Patent Laid-Open No. Sho 62-25187, page 2, upper right column,lines 3 to 11; Japanese Patent Laid-Open No. Sho 63-251163, page 2,lower left column, lines 7 to 14; Japanese Patent Laid-Open No. Hei1-205973, page 3, upper left column, line 11 to upper right column, line2; Japanese Patent Laid-Open No. Hei 3-115383, page 2, lower rightcolumn, line 16 to page 3, upper left column, line 11; Japanese PatentLaid-Open No. Hei 4-108887, page 2, lower left column, lines 1 to 9;Japanese Patent Laid-Open No. Hei 4-275387, page 2, right column, line27 to page 3, left column, line 12; Japanese Patent Laid-Open No. Hei4-363385, page 2, right column, lines 21 to 30, the entire contents ofwhich are incorporated herein by reference, and the like.

These other components may be used alone or in admixture of two or morekinds. In addition, the content of the other components is preferablyfrom 0.05 to 20% by weight, more preferably from 0.05 to 10% by weight,still more preferably from 0.05 to 5% by weight, of the roll-offreducing agent composition, from the viewpoint of exhibiting therespective functions and from the viewpoint of economic advantages.

The concentration of each component of the above-mentioned roll-offreducing agent composition is a preferable concentration duringpolishing, and it may be a concentration during the preparation of thecomposition. The composition is usually prepared as a concentrate, andthe concentrate is diluted upon use in many cases.

The roll-off reducing agent composition of the present invention can beprepared by adding one or more compounds selected from the groupconsisting of the carboxylic acids having 2 to 20 carbon atoms havingeither OH group or groups or SH group or groups, the monocarboxylicacids having 1 to 20 carbon atoms, and the dicarboxylic acids having 2to 3 carbon atoms, and salts thereof, and various additives, as occasiondemands in proper amounts to water and an abrasive, and mixing thecomponents by a known process.

It is preferable that the pH of the roll-off reducing agent compositionis appropriately adjusted depending upon the kinds and the requiredqualities and the like of the substrate to be polished. For instance,the pH of the roll-off reducing agent composition is preferably from 2to 12, from the viewpoints of the cleanability of the substrate and theanti-corrosiveness of the working machine, and from the viewpoint of thesafety of the operator. In addition, in a case where a substrate to bepolished is a substrate for precision parts which is mainly made of ametal such as an Ni—P plated aluminum alloy substrate, the pH ispreferably from 2 to 9, especially preferably from 3 to 8, from theviewpoints of increasing the polishing rate and improving the surfacequalities. When the roll-off reducing agent composition is used forpolishing a semiconductor wafer, a semiconductor element, or the like,especially for polishing a silicon substrate, a poly-silicon film, anSiO₂ film, or the like, the pH is preferably from 7 to 12, morepreferably from 8 to 12, especially preferably from 9 to 11, from theviewpoints of increasing the polishing rate and improving the surfacequalities. The pH can be adjusted by adding properly an inorganic acidsuch as nitric acid or sulfuric acid, an organic acid such as apolycarboxylic acid, an aminopolycarboxylic acid, or an amino acid, ametal salt or an ammonium salt thereof, or a basic substance such asaqueous ammonia, sodium hydroxide, potassium hydroxide or amine in adesired amount as occasion demands.

3. Process of Reducing Roll-off of Polished Substrate by Using Roll-offReducing Agent and Process for Producing Polished Substrate

The material for an object to be polished as representativelyexemplified by the substrate to be polished used in the presentinvention includes, for instance, metals or metalloids such as silicon,aluminum, nickel, tungsten, copper, tantalum and titanium; alloys madeof these metals as main components; glassy substances such as glass,glassy carbon and amorphous carbons; ceramic materials such as alumina,silicon dioxide, silicon nitride, tantalum nitride and titanium nitride;resins such as polyimide resins; and the like. Among them, it ispreferable that an object to be polished is made of a metal such asaluminum, nickel, tungsten or copper, or made of an alloy containingthese metals as the main components; or an object to be polished is asemiconductor substrate made of semiconductor elements containing thesemetals. Especially, in a case where the roll-off reducing agent of thepresent invention is used when polishing an aluminum alloy substrateplated with Ni—P, it is preferable because the extent of roll-off can bemade small.

The shape for the object to be polished is not particularly limited. Forinstance, those having shapes containing planar portions such as discs,plates, slabs and prisms, or shapes containing curved portions such aslenses can be subjects for polishing with the roll-off reducing agentcomposition of the present invention. Among them, those having thedisc-shaped objects are especially preferable in polishing.

The roll-off reducing agent of the present invention can be favorablyused in polishing the substrate for precision parts. For instance, theroll-off reducing agent is suitable for polishing substrates forprecision parts such as substrates for magnetic recording media formagnetic discs, optical discs, opto-magnetic discs, and the like;photomask substrates, optical lenses, optical mirrors, optical prismsand semiconductor substrates. The polishing of a semiconductor substratecomprises the steps of polishing a silicon wafer (bare wafer), formingseparation membrane for an embedding element, flattening an interlayerinsulating film, forming an embedded metal line, and forming embeddedcapacitor, and the like. The roll-off reducing agent composition of thepresent invention is especially suitable for polishing a magnetic discsubstrate.

In the process of reducing roll-off of the polished substrate using theroll-off reducing agent of the present invention, the extent of roll-offof the polished substrate can be remarkably reduced by polishing thesubstrate to be polished listed above with a polishing liquid comprisingthe roll-off reducing agent of the present invention, or the roll-offreducing agent composition of the present invention per se as apolishing liquid.

For instance, a substrate with reduced roll-off can be produced byclamping a substrate with polishing discs to which a polishing clothmade of nonwoven organic polymer fabric, is pasted; feeding a polishingliquid comprising the roll-off reducing agent of the present invention,or the roll-off reducing agent composition of the present invention to apolishing surface; and moving the polishing discs or the substrate, withapplying a given pressure.

The roll-off generated in the polished substrate in the presentinvention can be evaluated by determining the shape of the end surfacepart by using, for instance, a tracer or optical profilometer, andnumerically expressing the extent of how much more the end surface isgrounded as compared to the central portion of the disc in accordancewith the profile.

The method of numerically expressing roll-off is determined as follows.As shown in FIG. 1, three points, i.e. point A, point B and point C, aretaken on the detection curve which are given distances away from thecenter of the disc, the detection curve meaning the shape of the endsurface part of the polished substrate). Roll-off refers to a distance(D) between point B and a base line, wherein the base line is defined asa straight line connecting point A and point C. The term “having goodroll-off” refers to a value of D more approximating 0. The roll-offvalue refers to a value obtained by dividing D by ½ of the amount ofvariation in the thickness of the disc before and after polishing. Theroll-off value is preferably 0.2 μm/μm or less, more preferably 0.15μm/μm or less, still more preferably 0.10 μm/μm or less.

Here, the positions of point A, point B and point C may vary dependingupon the size of the object to be determined. In general, it ispreferable that point B is positioned at 0.5 mm away from the end of thedisc on the line connecting the end part and the center of the disc,that the point C is positioned at 2.5 mm away from the end, and thatthat the point A is positioned at 4.5 mm away from the end. Forinstance, in the case of 3.5 inch disc, it is preferable that point A,point B and point C are respectively positioned at 43 mm, 47 mm and 45mm away from the center of the disc.

In addition, in the polishing process of a substrate for precision partsor the like, by using the roll-off reducing agent of the presentinvention, there are advantages that not only the roll-off of thesubstrate can be remarkably reduced, but also that the polishing ratecan be increased. Also, in a case where one or more kinds selected fromoxalic acid, malic acid, tartaric acid, citric acid, gluconic acid, andsalts thereof are used as the roll-off reducing agent, it is preferablebecause the clogging of the abrasive grains and polishing grounds in thepolishing pad can be reduced, so that the deterioration of the polishingproperties such as polishing rate and surface qualities by using thepolishing pad for a long period of time can be prevented.

In this case, among the above-mentioned compounds, oxalic acid, tartaricacid, citric acid and salts thereof are preferable, and especiallycitric acid and salts thereof are preferable. In addition, in a casewhere the above-mentioned compounds are used in combination of two ormore kinds, especially preferable combinations are combinations of twoor more kinds selected from oxalic acid, tartaric acid, citric acid andsalts thereof, or combinations of one or more kinds selected from oxalicacid, tartaric acid, citric acid and salts thereof, with one or morekinds selected from malonic acid, glycolic acid, lactic acid, malicacid, gluconic acid and salts thereof. More preferable are combinationsof citric acid or a salt thereof with one or more kinds selected fromoxalic acid, glycolic acid, lactic acid, malic acid, tartaric acid andsalts thereof. Particularly preferable combinations are citric acid or asalt thereof with glycolic acid or a salt thereof.

The roll-off reducing agent composition of the present inventionespecially has an effect in the polishing process, and the roll-offreducing agent composition can be similarly applied to a process otherthan the polishing process, for instance, a lapping process, and thelike.

4. Polishing Composition

The polishing composition of the present invention can be roughlyclassified into the following three embodiments:

-   [Embodiment 1] A polishing composition comprising:    -   water;    -   an abrasive;    -   a roll-off reducing agent comprising one or more compounds        selected from the group consisting of carboxylic acids having 2        to 20 carbon atoms having either OH group or groups or SH group        or groups, monocarboxylic acids having 1 to 20 carbon atoms, and        dicarboxylic acids having 2 to 3 carbon atoms, and salts        thereof, and    -   an intermediate alumina.-   [Embodiment 2] A polishing composition comprising:    -   (A) one or more compounds selected from carboxylic acids having        2 to 20 carbon atoms having either OH group or groups or SH        group or groups, monocarboxylic acids having 1 to 20 carbon        atoms, and dicarboxylic acids having 2 to 3 carbon atoms, and        salts thereof;    -   (B) one or more compounds selected from polycarboxylic acids        having 4 or more carbon atoms and having neither OH group or        groups nor SH group or groups, aminopolycarboxylic acids, amino        acids and salts thereof; and    -   (C) one or more compounds selected from an intermediate alumina        and an alumina sol;    -   an abrasive; and    -   water.-   [Embodiment 3] A polishing composition comprising:    -   (A) one or more compounds selected from carboxylic acids having        2 to 20 carbon atoms having either OH group or groups or SH        group or groups, monocarboxylic acids having 1 to 20 carbon        atoms, and dicarboxylic acids having 2 to 3 carbon atoms, and        salts thereof; and    -   (B) one or more compounds selected from polycarboxylic acids        having 4 or more carbon atoms and having neither OH group or        groups nor SH group or groups, aminopolycarboxylic acids, amino        acids and salts thereof;    -   an abrasive; and    -   water.

EMBODIMENT 1

The polishing composition of Embodiment 1, as described above, compriseswater, an abrasive, a roll-off reducing agent, and an intermediatealumina.

As the abrasive usable in Embodiment 1, those abrasives which aregenerally used for polishing can be used. Examples of the abrasives arenot particularly limited, as long as they are the same ones as thoseused in the above-mentioned roll-off reducing agent composition.

The content of the abrasive is preferably from 1 to 40% by weight, morepreferably from 2 to 30% by weight, still more preferably from 3 to 15%by weight, of the polishing composition of Embodiment 1, from theviewpoints of having economic advantages and making the surfaceroughness of a polished object small, thereby making it possible toefficiently polish the substrate.

The roll-off reducing agent usable in Embodiment 1 may be the same onesas those mentioned above.

The content of the roll-off reducing agent is preferably from 0.01 to 5%by weight, more preferably from 0.015 to 4% by weight, still morepreferably from 0.03 to 2% by weight, of the polishing composition ofEmbodiment 1, from the viewpoints of reducing roll-off and havingeconomic advantages.

In addition, the intermediate alumina used in Embodiment 1 is a genericterm referring to alumina particles other than α-alumnina particles.Concrete examples thereof include γ-alumina particles, δ-aluminaparticles, θ-alumina particles, η-alumina particles, κ-aluminaparticles, and mixtures thereof. Among them, the following intermediatealuminas are preferable, from the viewpoints of increase in thepolishing rate and the effect of reducing the surface roughness of apolished object. The crystal forms of the intermediate aluminapreferably include γ-alumina, δ-alumina, θ-alumina, and mixturesthereof, more preferably γ-alumina and θ-alumina. In addition, theintermediate alumina has a specific surface area (BET method) ofpreferably from 30 to 300 m²/g, more preferably from 50 to 200 m²/g, andan average particle size of preferably from 0.01 to 5 μm, morepreferably from 0.05 to 5 μm, still more preferably from 0.1 to 3 μm,especially preferably from 0.1 to 1.5 μm. The average particle size canbe determined as a volume-average particle size by using a laserdiffraction method (for instance, one commercially available formHoriba, LTD. under the trade name of LA-920). In addition, the contentof each of the alkali metal and the alkaline earth metal in theintermediate alumina particles is preferably 0.1% by weight or less,more preferably 0.05% by weight or less, especially preferably 0.01% byweight or less.

For instance, in a case where aluminum hydroxide, an alumina sol or thelike which has a relatively large specific surface area and a lowcontent of the alkali metal and the alkaline earth metal is used as araw material, since there is little fusion of the intermediate aluminaproduced and the particle strength is small, no surface defects arecaused on a polished substrate, thereby making it especially effectivein reducing the surface roughness of a polished object.

As the raw material which can be used in the preparation of theintermediate alumina, there can be used, for instance, aluminumhydroxide, alumina sols, and the like, which can be represented by theformulas Al(OH)₃, Al₂O₃.3H₂O, AlOOH, Al₂O₃.H₂O, and Al₂O₃.nH₂O, whereinn is a number of 1 to 3. The specific surface area of the raw materialis preferably 10 m²/g or more, more preferably 30 m²/g or more,especially preferably 50 m²/g or more. In addition, the content of eachof the alkali metal and the alkaline earth metal in the raw material ispreferably 0.1% by weight or less, more preferably 0.05% by weight orless, especially preferably 0.03% by weight or less. Further, in a casewhere an intermediate alumina is prepared by thermally dehydratingaluminum hydroxide, a forcible introduction of a dry air or nitrogen gasduring baking is further effective in the reduction of surface defectsand surface roughness of the polished substrate. Here, theabove-mentioned thermal dehydration treatment can be carried out by aconventional method.

These intermediate aluminas are adjusted to a given particle size by wetpulverization or dry pulverization by using a pulverizer such as aball-mill, a beads-mill, a high-pressure homogenizer or a jet mill asoccasion demands.

Since the intermediate alumina is used together with the abrasive andthe roll-off reducing agent mentioned above, the polishing rate isincreased and surface defects such as pits are prevented, and thereduction in the surface roughness of the polished substrate can befurther accelerated.

It is desired that the content of the intermediate alumina in thepolishing composition of Embodiment 1 is from 1 to 100 parts by weight,preferably from 2 to 70 parts by weight, more preferably from 4 to 40parts by weight, based on 100 parts by weight of the abrasive, from theviewpoints of economic advantages, an accelerated effect of polishing,and an effect of reducing the surface roughness of the polishedsubstrate, and from the viewpoint of obtaining capability of preventingsurface defects such as pits.

Water in the polishing composition of Embodiment 1 is used as a medium,and the content of water is preferably from 40 to 98% by weight, morepreferably from 50 to 97% by weight, especially preferably from 60 to95% by weight, from the viewpoint of being capable of efficientlypolishing the object to be polished.

EMBODIMENT 2

The polishing composition of Embodiment 2, as described above, comprisesone or more compounds selected from Compounds (A), one or more compoundsselected from Compounds (B), one or more compounds selected fromCompounds (C), an abrasive, and water.

Compounds (A) usable in Embodiment 2 are the same as the roll-offreducing agent usable in Embodiment 1 mentioned above.

The content of Compounds (A) is preferably from 0.01 to 5% by weight,more preferably from 0.015 to 3% by weight, still more preferably from0.03 to 2% by weight, of the polishing composition of Embodiment 2, fromthe viewpoint of improving roll-off and from the viewpoint of havingeconomic advantages.

Compounds (B) usable in Embodiment 2 have an action of increasing thepolishing rate. Compounds (B) include polycarboxylic acids having 4 ormore carbon atoms and having neither OH group or groups nor SH group orgroups, aminopolycarboxylic acids, amino acids and salts thereof.

Among the polycarboxylic acids having 4 or more carbon atoms and havingneither OH group nor groups or SH group or groups, those having 4 to 20carbon atoms are preferable, more preferably 4 to 10 carbon atoms, fromthe viewpoint of increasing the polishing rate. Also, for the sameviewpoint as above, the aminopolycarboxylic acids preferably have anumber of amino groups in one molecule of from 1 to 6, more preferablyfrom 1 to 4, a number of carboxyl groups in one molecule of preferablyfrom 1 to 12, more preferably 2 to 8, and a number of carbon atoms ofpreferably from 1 to 30, preferably from 1 to 20. For the same viewpointas above, the amino acids preferably have a number of carbon atoms ofpreferably from 2 to 20, preferably from 2 to 10. Among them,polycarboxylic acids having 4 or more carbon atoms and having neither OHgroup or groups nor SH group or groups, aminopolycarboxylic acids, andsalts thereof are preferable, from the viewpoint of increasing thepolishing rate.

Concrete examples thereof include succinic acid, maleic acid, fumaricacid, glutaric acid, citraconic acid, itaconic acid, tricarballylicacid, adipic acid, propane-1,1,2,3-tetracarboxylic acid,butane-1,2,3,4-tetracarboxylic acid, diglycolic acid, nitrilotriaceticacid, ethylenediaminetetraacetic acid (EDTA),diethylenetriaminepentaacetic acid (DTPA),hydroxyethylethylenediaminetetraacetic acid (HEDTA),triethylenetetraminehexaacetic acid (TTHA), dicarboxymethylglutamic acid(GLDA), glycine, alanine, and the like.

Among them, succinic acid, maleic acid, fumaric acid, glutaric acid,citraconic acid, itaconic acid, tricarballylic acid, adipic acid,diglycolic acid, nitrilotriacetic acid, ethylenediaminetetraacetic acidand diethylenetriaminepentaacetic acid are preferable, and succinicacid, maleic acid, fumaric acid, citraconic acid, itaconic acid,tricarballylic acid, diglycolic acid, ethylenediaminetetraacetic acidand diethylenetriaminepentaacetic acid are more preferable.

In addition, the salts of these acids, i.e. salts of polycarboxylicacids having 4 or more carbon atoms and having neither OH group orgroups nor SH group or groups, salts of aminopolycarboxylic acids andsalts of amino acids, are not particularly limited. Concretely, thereare included salts with a metal, ammonium, an alkylammonium, an organicamine, and the like. Concrete examples of the metal include metalsbelonging to Group 1A, 1B, 2A, 2B, 3A, 3B, 4A, 6A, 7A or 8 of thePeriodic Table (long period form). Among these metals, from theviewpoint of increasing the polishing rate, the metals belonging toGroup 1A, 3A, 3B, 7A or 8 of the Periodic Table are preferable, and themetals belonging to Group 1A, 3A, 3B or 8 of the Periodic Table are morepreferable. Sodium and potassium belonging to Group 1A, cerium belongingto Group 3A, aluminum belonging to Group 3B and iron belonging to Group8 are most preferable.

Concrete examples of the alkylammonium include tetramethylammonium,tetraethylammonium, tetrabutylammonium, and the like.

Concrete examples of the organic amine include dimethylamine,trimethylamine, alkanolamines, and the like.

Among these salts, ammonium salts, sodium salts, potassium salts andaluminum salts are especially preferable.

These compounds of Compounds (B) can be used alone or in admixture oftwo or more kinds.

A total content of Compounds (B) is preferably from 0.01 to 10% byweight, more preferably from 0.02 to 7% by weight, still more preferablyfrom 0.03 to 5% by weight, of the polishing composition of Embodiment 2,from the viewpoint of the effect of accelerating polishing, theviewpoint of economic advantages, and the viewpoint of improvement inthe surface qualities.

Also, in Embodiment 2, more preferable combinations of Compounds (A)with Compounds (B) are combinations of one or more compounds selectedfrom Compounds (A), acetic acid, oxalic acid, malonic acid, glycolicacid, lactic acid, malic acid, glyoxylic acid, tartaric acid, citricacid, gluconic acid, and salts thereof, with one or more compoundsselected from Compounds (B), succinic acid, maleic acid, fumaric acid,glutaric acid, citraconic acid, itaconic acid, adipic acid,tricarballylic acid, diglycolic acid, nitrilotriacetic acid,ethylenediaminetetraacetic acid, diethylenetriaminepentaacetic acid andsalts thereof, from the viewpoints of increasing the polishing rate andreducing roll-off. Still more preferable are combinations of one or morecompounds selected from Compounds (A), oxalic acid, malonic acid,glycolic acid, lactic acid, malic acid, glyoxylic acid, tartaric acid,citric acid, gluconic acid, and salts thereof, with one or morecompounds selected from Compounds (B), succinic acid, maleic acid,fumaric acid, citraconic acid, itaconic acid, tricarballylic acid,diglycolic acid, ethylenediaminetetraacetic acid,diethylenetriaminepentaacetic acid and salts thereof Especiallypreferable are combinations of one or more compounds selected fromCompounds (A), glycolic acid, oxalic acid, tartaric acid, citric acid,malonic acid, and salts thereof, with one or more compounds selectedfrom Compounds (B), succinic acid, maleic acid, itaconic acid, fumaricacid, ethylenediaminetetraacetic acid, diethylenetriaminepentaaceticacid and salts thereof In addition, in a case where one or morecompounds selected from oxalic acid, malic acid, tartaric acid, citricacid, gluconic acid and salts thereof are used as Compounds (A), it ispreferable, because clogging of the abrasive grains and polishinggrounds in the polishing pad can be reduced, so that the deteriorationof the polishing properties such as polishing rate and surface qualitiesby using the polishing pad for a long period of time can be prevented.

In this case, among Compounds (A), oxalic acid, tartaric acid, citricacid, and salts thereof are preferable, and citric acid and saltsthereof are especially preferable. In addition, in a case where two ormore kinds of Compounds (A) are used in combination, especiallypreferable combinations are combinations of two or more kinds selectedfrom oxalic acid, tartaric acid, citric acid and salts thereof; orcombinations of one or more kinds selected from oxalic acid, tartaricacid, citric acid and salts thereof with one or more kinds selected frommalonic acid, glycolic acid, lactic acid, malic acid, gluconic acid andsalts thereof. More preferable combinations are combinations of citricacid or a salt thereof with one or more kinds selected from oxalic acid,glycolic acid, lactic acid, malic acid, tartaric acid and salts thereof.Especially preferable combinations are combinations of citric acid or asalt thereof with glycolic acid or a salt thereof.

Compounds (C) used in Embodiment 2 comprise an intermediate alumina andalumina sol. The intermediate alumina is a generic term referring toalumina particles other than α-alumina particles. The intermediatealumina may be the same ones as those usable in Embodiment 1 mentionedabove.

In addition, the alumina sol refers to those which can be represented bythe formulas AlOOH, AlOOH.nH₂O, wherein n is a number of 1 to 3, forinstance, Al₂O₃.H₂O and the like. The crystal forms of the alumina solinclude boehmite, pseudo-boehmite and amorphous. The alumina sol can beprepared by subjecting aluminum hydroxide, for instance, gibbsite, to ahydrothermal treatment at 250° C. or so, or hydrolyzing an aluminumalcoholate. The alumina sol has an average particle size of preferablyfrom 0.01 to 5 μm, more preferably from 0.05 to 5 μm, still morepreferably from 0.1 to 3 μm, especially preferably from 0.1 to 1.5 μm.The average particle size can be determined as a volume-average particlesize by using a laser diffraction method. The alumina sol has a specificsurface area (BET method) of preferably from 30 to 300 m²/g, morepreferably from 50 to 200 m²/g.

Since the intermediate alumina and the alumina sol in Compounds (C) areused together with Compounds (A) and Compounds (B), the effects that thepolishing rate is increased and surface defects such as pits areprevented, and the reduction in the surface roughness of the polishedobject can be further accelerated. In this case, the intermediatealumina and the alumina sol in Compounds (C) can be used alone or inadmixture. Especially, the intermediate alumina is more preferable, fromthe viewpoints of an increase in the polishing rate, an extent of theeffect of preventing surface defects and the like, and an effect ofreducing the surface roughness of a polished object.

A total content of Compounds (C) in the polishing composition ofEmbodiment 2 is preferably from 1 to 100 parts by weight, morepreferably from 2 to 70 parts by weight, still more preferably from 4 to40 parts by weight, based on 100 parts by weight of the abrasive, fromthe viewpoints of economic advantages, the effect of acceleratingpolishing, the effect of reducing the surface roughness of a polishedobject, and from the viewpoint of obtaining the capability of preventingsurface defects such as pits.

As the abrasive usable in Embodiment 2, those abrasives which aregenerally used for polishing can be used. The abrasives may be the sameones as those used in the above-mentioned roll-off reducing agentcomposition.

The content of the abrasive is preferably from 1 to 40% by weight, morepreferably from 2 to 30% by weight, still more preferably from 3 to 15%by weight, of the polishing composition of Embodiment 2, from theviewpoints of having economic advantages and making the surfaceroughness of a polished object small, thereby making it possible toefficiently polish the object to be polished.

Water in the polishing composition of Embodiment 2 is used as a medium,and the content of water is preferably from 40 to 98% by weight, morepreferably 50 to 97% by weight, especially preferably from 60 to 95% byweight, from the viewpoint of being capable of efficiently polishing theobject to be polished.

EMBODIMENT 3

The polishing composition of Embodiment 3, as described above, comprisesone or more compounds selected from Compounds (A), one or more compoundsselected from Compounds (B), an abrasive, and water.

Compounds (A) usable in Embodiment 3 have an action of improvingroll-off caused in the polished substrate, and are the same ones asthose exemplified as Compounds (A) in Embodiment 2 mentioned above canbe used.

The content of Compounds (A) is preferably from 0.01 to 5% by weight,more preferably from 0.015 to 3% by weight, still more preferably from0.03 to 2% by weight, of the polishing composition of Embodiment 3, fromthe viewpoints of improving roll-off and having economic advantages.

Compounds (B) usable in Embodiment 3 have an action of increasing thepolishing rate, and the same ones as those Compounds (B) which are usedin Embodiment 2 mentioned above can be used.

The content of Compounds (B) is preferably from 0.01 to 10% by weight,more preferably from 0.02 to 7% by weight, still more preferably from0.03 to 5% by weight, of the polishing composition of Embodiment 3, fromthe viewpoint of the effect of accelerating polishing, the viewpoint ofeconomic advantages, and the viewpoint of improvement in the surfacequalities.

As to the combinations of Compounds (A) and Compounds (B), the same onesas those combinations which are mentioned in Embodiment 2 can be used.

As the abrasive usable in Embodiment 3, those abrasives which aregenerally used for polishing can be used. Examples of the abrasives maybe the same ones as those used in the above-mentioned roll-off reducingagent composition.

The content of the abrasive is preferably from 1 to 40% by weight, morepreferably from 2 to 30% by weight, still more preferably from 3 to 15%by weight, of the polishing composition of Embodiment 3, from theviewpoints of having economic advantages and making the surfaceroughness of a polished object small, thereby making it possible toefficiently polish the substrate.

Water in the polishing composition of Embodiment 3 is used as a medium,and the content of water is preferably from 40 to 98% by weight, morepreferably from 50 to 97% by weight, especially preferably from 60 to95% by weight, from the viewpoint of being capable of efficientlypolishing the object to be polished.

The polishing composition of the present invention, as representativelyexemplified by Embodiments 1 to 3 described above, can contain othercomponents as occasion demands. As other components, there are includedorganic acids and salts other than the above-mentioned roll-off reducingagent. The other components include, for instance, organic acids such aspolycarboxylic acids, aminopolycarboxylic acids and amino acids, andsalts thereof, inorganic acids and salts thereof, oxidizing agents,thickeners, dispersants, anticorrosive agents, basic substances,surfactants, and the like. Concrete examples of the organic acids andsalts thereof, inorganic acids and salts thereof, and the oxidizingagents may be the same ones used in the above-mentioned roll-offreducing agent composition.

These other components may be used alone or in admixture of two or morekinds. In addition, the content of the other components is preferablyfrom 0.05 to 20% by weight, more preferably from 0.05 to 10% by weight,still more preferably from 0.05 to 5% by weight, of the polishingcomposition, from the viewpoint of increasing the polishing rate, fromthe viewpoint of exhibiting the respective functions and from theviewpoint of economic advantages.

The concentration of each component of the above-mentioned polishingcomposition is a preferable concentration during polishing, and it maybe a concentration during the preparation of the composition. Thecomposition is usually prepared as a concentrate, and the concentrate isdiluted upon use in many cases.

The process for preparing the polishing composition of the presentinvention includes the following:

The polishing composition of Embodiment 1 can be prepared by addingtogether in proper amounts an abrasive, a roll-off reducing agent, anintermediate alumina, and water, and various additives, as occasiondemands, each of which is exemplified above, and mixing the componentsby a known process.

Also, the polishing composition of Embodiment 2 can be prepared byadding together in proper amounts Compounds (A), Compounds (B),Compounds (C), an abrasive, water, and various additives as occasiondemands, each of which is exemplified above, and mixing the componentsby a known process.

In addition, the polishing composition of Embodiment 3 can be preparedby adding together in proper amounts Compounds (A), Compounds (B), anabrasive, water, and various additives as occasion demands, each ofwhich is exemplified above, and mixing the components by a knownprocess.

It is preferable that the pH of the polishing composition of the presentinvention is appropriately adjusted depending upon the kinds and therequired qualities and the like of the object to be polished. Forinstance, the pH of the polishing composition is preferably from 2 to12, from the viewpoints of the cleanability of the substrate andanti-corrosiveness of the working machine, and from the viewpoint of thesafety of the operator. In addition, in a case where an object to bepolished is a substrate for precision parts which is mainly made of ametal such as an Ni—P plated aluminum alloy substrate, the pH is morepreferably from 2 to 9, especially preferably from 3 to 8, from theviewpoints of increasing the polishing rate and improving the surfacequalities. When the polishing composition is used for polishing asemiconductor wafer, a semiconductor element, or the like, especiallypolishing a silicon substrate, a poly-silicon film, an SiO₂ film, or thelike, the pH is preferably from 7 to 12, more preferably from 8 to 12,especially preferably from 9 to 11, from the viewpoints of increasingthe polishing rate and improving the surface qualities. The pH can beadjusted by adding properly an inorganic acid such as nitric acid orsulfuric acid, an organic acid, or a basic substance such as aqueousammonia, sodium hydroxide, potassium hydroxide in a desired amount asoccasion demands.

5. Polishing Process of Substrate to be Polished by Using PolishingComposition

The polishing process of a substrate to be polished of the presentinvention comprises polishing a substrate to be polished by using thepolishing composition of the present invention, or preparing a polishingliquid by mixing each component so as to give the composition of thepolishing composition of the present invention. Especially, thesubstrate for precision parts can be suitably produced.

The material for the object to be polished as representativelyexemplified by the substrate to be polished used in the presentinvention may be the same ones as those to which the above-mentionedroll-off reducing agent composition is used. Especially, in a case wherethe polishing composition of the present invention is used whenpolishing an aluminum alloy substrate plated with Ni—P, it is preferablebecause the roll-off can be reduced, the polishing rate can beincreased, and the surface roughness of a polished object can be reducedwithout causing surface defects.

The shape for the object to be polished is not particularly limited, andmay be the same ones as those for the above-mentioned roll-off reducingagent composition.

The polishing composition of the present invention can be favorably usedin polishing the substrate for precision parts. For instance, thepolishing composition is suitable for polishing substrates for magneticrecording media for magnetic discs, optical discs, opto-magnetic discs,and the like; photomask substrates, optical lenses, optical mirrors,optical prisms and semiconductor substrates. The polishing of thesemiconductor substrates comprises the steps of polishing a siliconwafer (bare wafer), forming separation membrane for an embeddingelement, flattening an interlayer insulating film, forming an embeddedmetal line, and forming embedded capacitor, and the like. The polishingcomposition of the present invention is especially suitable forpolishing a magnetic disc substrate. Among the magnetic disc substrates,aluminum magnetic disc substrates plated with Ni—P can be especiallysuitably used.

6. Process for Producing Polished Substrate by Using PolishingComposition

In addition, a process for producing a polished substrate by using thepolishing composition of the present invention includes, for instance, aprocess comprising clamping a substrate to be polished with polishingdiscs to which a polishing cloth made of nonwoven organic polymerfabric, is pasted; feeding a polishing composition of the presentinvention to a polishing surface; and moving the polishing discs or thesubstrate, with applying a given pressure, thereby reducing roll-off andsurface roughness of the polished object, to give a substrate withoutsurface defects. Here, the roll-off generated in the polished substratein the present invention can be evaluated in the same manner asdescribed above.

As described above, by using the polishing composition of the presentinvention, a high-quality substrate with reduced surface roughness andreduced roll-off as well as increased polishing rate can be producedwith high production efficiency without generating surface defects onthe polished substrate. In addition, when a polishing compositioncomprising one or more compounds selected from oxalic acid, malic acid,tartaric acid, citric acid, gluconic acid and salts thereof is used, itis preferable because clogging of the abrasive grains and polishinggrounds in the polishing pad can be reduced, so that the deteriorationof the polishing properties such as polishing rate and surface qualitiesby using the polishing pad for a long period of time can be prevented.

In this case, among the above-mentioned compounds, oxalic acid, tartaricacid, citric acid and salts thereof are preferable, and especiallycitric acid and salts thereof are preferable. When these compounds areused in combination of two or more kinds, especially preferablecombinations are combinations of two or more kinds selected from oxalicacid, tartaric acid, citric acid and salts thereof, or combinations ofone or more kinds selected from oxalic acid, tartaric acid, citric acidand salts thereof with one or more kinds selected from malonic acid,glycolic acid, lactic acid, malic acid, gluconic acid and salts thereof.More preferable are combinations of citric acid or a salt thereof withone or more kinds selected from oxalic acid, glycolic acid, lactic acid,malic acid, tartaric acid and salts thereof. Especially preferablecombinations are combinations of citric acid or a salt thereof withglycolic acid or a salt thereof.

The polishing composition of the present invention especially has aneffect in the polishing process, and the polishing composition can besimilarly applied to a process other than the polishing process, forinstance, a lapping process, and the like.

EXAMPLES Examples I-1 to I-10 and Comparative Examples I-1 to I-5

There were mixed together 7 parts by weight of an abrasive [α-alumina(purity: about 99.9%) having primary average particle size: 0.23 μm, andsecondary average particle size: 0.5 μm], a given amount of a roll-offreducing agent used in Examples or a compound used in ComparativeExamples as listed in Table 1, and balance ion-exchanged water, withstirring. Here, the pH of each composition in Examples I-1 to I-10 andComparative Examples I-2 to I-4 was adjusted to 4 with an aqueousammonia, and the pH of each composition in Comparative Examples I-1 andI-5 was adjusted to 4 with nitric acid, to give 100 parts by weight ofeach roll-off reducing agent composition of Examples I-1 to I-10 andComparative Examples I-1 to I-5.

Using each of the resulting roll-off reducing agent compositions, asubstrate surface made of an Ni—P plated aluminum alloy, the substratesurface having an average deviation, of all points from plane fit totest part surface Ra of 0.2 μm, as determined by Talystep commerciallyavailable from Rank Taylor-Hobson Limited (size of tip end ofprofilometer: 25 μm×25 μm, by-pass filter: 80 μm, measurement length:0.64 mm), a thickness of 0.8 mm and a diameter of 95 mm was polishedwith a double-sided processing machine under Set Conditions I forDouble-Sided Processing Machine given below, to give a polished Ni—Pplated, aluminum alloy substrate usable for magnetic recording media.

Set Conditions I for Double-Sided Processing Machine are as follows.

Set Conditions I for Double-Sided Processing Machine

-   Double-sided processing machine: double-sided processing machine,    Model 9B, manufactured by SPEEDFAM CO., LTD.-   Processing pressure: 9.8 kPa-   Polishing Pad: “POLYTEX DG-H” (manufactured by Rodel Nitta K.K.).-   Disc rotational speed: 50 r/min-   Feeding flow rate for a polishing composition: 100 ml/min-   Polishing time period: 5 minutes-   Number of substrate introduced; 10

After polishing, the value of roll-off generated in the polishedsubstrate was determined by the method described below, and expressed asa relative value on the basis of the value of Comparative Example I-2.Also, the thickness of an Ni—P plated aluminum alloy substrate ofExamples was determined by using a thickness tester (a laser thicknesstester, commercially available from Mitsutoyo Corporation, ModelLGH-110/LHC-11IN). A rate of decrease in the thickness was obtained fromthe changes in the thickness of the aluminum alloy substrate before andafter polishing, and expressed as a relative value (relative polishingrate) on the basis of the polishing rate of Comparative Example I-1.

The results are shown in Table 1.

-   Method for Determination of Roll-off-   Determination device: Mitsutoyo form tracer SV-C624-   Tip end radius of profilometer: 2 μm (Code No. 178-381)-   Pressure at profilometer: 0.7 mN or less-   5 Speed: 0.2 mm/s-   Analyzing software: SV-600 Fine Profile Analysis System, Version    1.01-   Filter: LPF (Gaussian) 0.800 mm

Using the device as specified above, the shape of the end part of thedisc at 42.5 mm to 47.5 mm away from the center of the disc wasdetermined, and D was obtained by using an analyzing software inaccordance with the above determination method by taking points A, B andC at 43 mm away from the center of the disc, at 47 mm away from thecenter, and at 45 mm away from the center, respectively. The valueobtained by dividing D by ½ the amount of change of thickness of thedisc before and after polishing is defined as the roll-off value. TABLE1 Polishing Amount Roll-Off Rate (Parts by (Relative (Relative AddedCompound Weight) Value) Value) Ex. No. I-1 Lactic Acid 0.81 0.54 1.6 I-2Glycolic Acid 0.69 0.23 1.4 I-3 Tartaric Acid 0.68 0.24 1.3 I-4 CitricAcid 0.58 0.41 1.5 I-5 Malic Acid 0.61 0.43 1.3 I-6 Glyoxylic Acid 0.830.34 1.3 I-7 Oxalic Acid 0.29 0.14 1.1 I-8 Malonic Acid 0.47 0.15 1.1I-9 Acetic Acid 0.54 0.61 1.2 I-10 Glycolic Acid 0.69 0.21 1.4 CitricAcid 0.10 Comp. Ex. No. I-1 None — Undeter- 1.0 minable #1 I-2 AluminumNitrate 0.60 1.0 #2 — I-3 Succinic Acid 0.53 0.83 — I-4 Aluminumammonium0.83 1.54 — Ethylenediamine- tetraacetate I-5 Glycine 0.68 0.93 —#1: Ski jump was caused, so that the roll-off was undeterminable.#2: The roll-off value was 0.31 μm/μm.

It is clear from the results in Table 1 that all of the roll-offreducing agent compositions obtained in Examples I-1 to I-10 haveremarkably reduced roll-off, as compared to the roll-off reducing agentcomposition obtained in Comparative Examples I-1 to 1-5. Also, it isalso found that the roll-off reducing agent compositions of Examples I-1to I-10 each of which comprises the roll-off reducing agent of thepresent invention have increased polishing rates, as compared with thatof Comparative Example I-1.

Further, the roll-off reducing agent composition prepared in each ofExample I-4, Example I-10 and Comparative Example I-3 was subjected topolishing evaluation mentioned above for 20 repeated times, and a ratioof a twentieth relative polishing rate to the first relative polishingrate was determined as a measure for an ability of preventing padclogging. As a result, the ratio of a twentieth relative polishing rateto the first relative polishing rate in the roll-off reducing agentcomposition of Example I-4 was 0.97, the ratio in the roll-off reducingagent composition of Example I-10 was 0.95, and the ratio in thecomposition of Comparative Example I-3 was 0.62.

It is clear from the evaluation results of ability of preventing padclogging for Examples I-4 and I-10 and Comparative Example I-3 thatExamples I-4 and I-10 exhibit little deterioration in the polishing rateas compared to that in Comparative Example I-3, thereby exhibiting anexcellent ability for preventing pad clogging.

Preparation Example II-1 for Intermediate Alumina

An alumina vessel (200 mm in length×100 mm in width×100 mm in height)was charged with 100 g of pseudo-boehmite particles having an averageparticle size of 25 μm, a specific surface area of 250 m²/g, an alkalimetal content of 0.003% by weight, and an alkaline earth metal contentof 0.01% by weight. The pseudo-boehmite particles were heated in amuffle furnace at a heating rate of 50° C./minute, and baked at a bakingtemperature of 930° C. for 4 hours with nitrogen gas stream at a flowrate of 5 L/minute, to give an intermediate alumina. The intermediatealumina was transferred to a 2-L alumina ball-mill, and ion-exchangedwater was added thereto to prepare a 30% by weight slurry. Thereafter,alumina balls of 3 mm in diameters were introduced into the ball-mill todisrupt the slurry, to prepare intermediate alumina particles. Theprepared intermediate alumina particles were found to have the crystalform of γ-alumina by analysis of X-ray diffraction peaks, and had anaverage particle size of 0.3 μm, a specific surface area of 150 m²/g, analkali metal content of 0.005% by weight, and an alkaline earth metalcontent of 0.01% by weight.

Examples II-1 to II-6 and Comparative Examples II-1 to II-5

There were mixed together an abrasive [α-alumina (purity: about 99.9%)having primary average particle size: 0.25 μm and secondary averageparticle size: 0.8 μm], a roll-off reducing agent, an intermediatealumina (γ-alumina) obtained in Preparation Examples II-1, and balanceion-exchanged water, to give a composition as shown in Table 2 withstirring. Here, the pH of each composition in Examples II-1 to II-5 andComparative Examples II-2, II-3 and II-5 was adjusted to 4.0 with anaqueous ammonia, and the pH of each composition in Comparative ExamplesII-1 and II-4 was adjusted to 4.0 with nitric acid, to give 100 parts byweight of each polishing composition of Examples II-1 to II-6 andComparative Examples II-1 to II-5. TABLE 2 α-Alumina Roll-Off AmountIntermediate Amount (Parts by Reducing (Parts by Alumina or (Parts byWeight) Agent Weight) Alumina Sol¹⁾ Weight Example No. II-1 7 GlycolicAcid 0.15 Intermediate 1 Alumina II-2 7 Malic Acid 0.15 Intermediate 1Alumina II-3 7 Tartaric Acid 0.15 Intermediate 1 Alumina II-4 7 MalonicAcid 0.15 Intermediate 1 Alumina II-5 7 Citric Acid 0.15 Intermediate 1Alumina II-6 7 Glycolic Acid 0.15 Intermediate 1 Alumina Citric Acid0.05 Comparative Example No. II-1 7 None — None — II-2 7 Diammonium 0.15Intermediate 1 Ethylenediamine- Alumina tetraacetate II-3 7 SuccinicAcid 0.15 Alumina Sol 1 II-4 7 Gluconic Acid 0.15 Alumina Sol 1 II-5 7Glycolic Acid 0.15 Alumina Sol 1¹⁾Commercially available from Nissan Chemical Industries, Ltd, under thetrade name of Alumina Sol-200

Using each of the resulting polishing compositions, a substrate surfacemade of an Ni—P plated aluminum alloy, the substrate surface having anaverage deviation, of all points from plane fit to test part surface Raof 0.2 μm, as determined by the following method, a thickness of 0.8 mmand a diameter of 95 mm was polished with a double-sided processingmachine under Set Conditions II for Double-Sided Processing Machinegiven below, to give a polished Ni—P plated, aluminum alloy substrateusable for magnetic recording media.

Set Conditions II for Double-Sided Processing Machine are as follows.

Set Conditions II for Double-Sided Processing Machine

-   Double-sided processing machine: double-sided processing machine,    Model 9B, manufactured by SPEEDFAM CO., LTD.-   Processing pressure: 9.8 kPa-   Polishing Pad: “POLYTEX DG-H” (manufactured by Rodel Nitta K.K.).-   Disc rotational speed: 55 r/min-   Feeding flow rate for a polishing composition: 100 mL/min-   Polishing time period: 4 minutes-   Number of substrate introduced: 10

After polishing, the thickness of an Ni—P plated aluminum alloysubstrate of Examples was determined by using a thickness tester (alaser thickness tester, commercially available from MitsutoyoCorporation, Model LGH-110/LHC-11N). A rate of decrease in the thicknesswas obtained from the changes in the thickness of the aluminum alloysubstrate before and after polishing, and expressed as a relative value(relative polishing rate) on the basis of the polishing rate ofComparative Example II-1.

In addition, the surface roughness (average deviation, of all pointsfrom plane fit to test part surface Ra) and pits (surface defects) ofeach substrate after polishing were determined in accordance with thefollowing methods, and roll-off was determined in the same manner asabove. Here, the average deviation, of all points from plane fit to testpart surface Ra was obtained as a relative value (relative roughness) onthe basis of the surface roughness of Comparative Example II-1. Inaddition, the roll-off was obtained as a relative value (relativeroll-off) on the basis of the roll-off value of Comparative ExampleII-2. The results are shown in Table 3.

[Average Deviation, of All Points from Plane Fit to Test Part SurfaceRa]

Determined under the following conditions by using Talystep commerciallyavailable from Rank Taylor-Hobson Limited

-   Size of tip end of profilometer: 25 μm×25 μm-   By-pass filter: 80 μm-   Measurement length: 0.64 mm    [Surface Defects (Pits)]

The surface of each substrate was observed with an optical microscope(differential interference microscope) at a magnification of 200 timesat an interval of 30° for 12 locations, and the number of pits wascounted and evaluated as follows:

-   S: 0-   A: 1 to 3-   B: 4 to 10

C: 10 or more TABLE 3 Evaluation of Properties Polishing Surface SurfaceRate Roughness Defects Roll-Off (−) (−) (Pits) (−) Example No. II-1 1.60.68 S 0.21 II-2 1.7 0.65 S 0.23 II-3 1.6 0.70 S 0.24 II-4 1.4 0.65 S0.25 II-5 1.7 0.72 S 0.25 II-6 1.6 0.70 S 0.20 Comparative Example No.II-1 1 1 C Undeter- minable*¹ II-2 1.6 0.70 S 1*² II-3 1.5 1.2 A 0.83II-4 1.4 1.1 A 0.40 II-5 1.1 1.1 A 0.25*¹Ski jump was caused, so that the roll-off was undeterminable.*²The roll-off value was 0.36 μm/μm.

It is clear from the results in Table 3 that all of the polishingcompositions obtained in Examples II-1 to II-6 have high polishingrates, and especially as compared with the polishing compositionsobtained in Comparative Examples II-1 to II-5, the polishingcompositions obtained in Examples II-1 to II-6 have reduced surfaceroughness, no surface defects, and markedly reduced roll-off in thepolished substrate.

Further, the polishing composition prepared in each of Example II-5,Example II-6 and Comparative Example II-3 was subjected to polishingevaluation mentioned above for 20 repeated times, and a ratio of atwentieth relative polishing rate to the first relative polishing ratewas determined as a measure for an ability of preventing pad clogging.As a result, the ratio of a twentieth relative polishing rate to thefirst relative polishing rate in the polishing composition of ExampleII-5 was 0.91, the ratio in the polishing composition of Example II-6was 0.90, and the ratio in t he polishing composition of ComparativeExample II-3 was 0.50.

It is clear from the evaluation results of ability of preventing padclogging for the polishing compositions of Examples II-5 and II-6exhibit excellent ability for preventing pad clogging, as compared withthat of Comparative Example II-3.

Preparation Example II-1 for Intermediate Alumina

An alumina vessel (200 mm in length×100 mm in width×100 mm in height)was charged with 100 g of pseudo-boehmite particles having an averageparticle size of 15 μm, a specific surface area of 240 m²/g, an alkalimetal content of 0.002% by weight, and an alkaline earth metal contentof 0.01% by weight. The pseudo-boehmite particles were heated in amuffle furnace at a heating rate of 50° C./minute, and baked at a bakingtemperature of 900° C. for 4 hours with nitrogen gas stream at a flowrate of 5 L/minute, to give an intermediate alumina. The intermediatealumina was transferred to a 2-L alumina ball-mill, and ion-exchangedwater was added thereto to prepare a 30% by weight slurry. Thereafter,alumina balls of 3 mm in diameters were introduced into the ball-mill todisrupt the slurry, to prepare intermediate alumina particles. Theprepared intermediate alumina particles were found to have the crystalform of γ-alumina by analysis of X-ray diffraction peaks, and had anaverage particle size of 0.3 μm, a specific surface area of 120 m²/g, analkali metal content of 0.003% by weight, and an alkaline earth metalcontent of 0.01% by weight.

Examples III-1 to III-8 and Comparative Examples III-1 to III-5

There were mixed together an abrasive [α-alumina (purity: about 99.9%)having primary average particle size: 0.25 μm, and secondary averageparticle size: 0.65 μm], Compounds (A), Compounds (B), Compounds (C) [anintermediate alumina (γ-alumina) obtained in Preparation Examples III-1or an alumina sol (boehmite)], and balance ion-exchanged water, to givea composition as shown in Table 4 with stirring. Here, the pH of eachcomposition in Examples III-1 to III-8 and Comparative Examples III-1 toIII-5 was adjusted to 4.0 or 7.0 with nitric acid or an aqueous ammonia,to give 100 parts by weight of each polishing composition of ExamplesIII-1 to III-8 and Comparative Examples III-1 to III-5. TABLE 4Compounds (A) Compounds (B) Compounds (C) α-Alumina Amount Amount Amount(parts by (parts by (parts by (parts by weight) Compound weight)Compound weight) Compound weight) pH Ex. No. III-1 7 Glycolic 0.15Aluminumammonium ethylene- 0.8 Intermediate 1 4 acid diaminetetraacetateAlumina III-2 7 Glycolic 0.15 Maleic acid 0.5 Intermediate 1 7 acidAlumina III-3 7 Oxalic 0.15 Itaconic acid 0.5 Intermediate 1 7 acidAlumina III-4 7 Tartaric 0.15 Fumaric acid 0.5 Intermediate 1 7 acidAlumina III-5 7 Citric 0.15 Succinic acid 0.5 Intermediate 1 7 acidAlumina III-6 7 Glycolic 0.15 Diammonium ethylenediamine 0.8 AluminaSol*¹ 1.5 4 acid tetraacetate III-7 7 Glycolic 0.15 Glycine 0.5Intermediate 1 7 acid Alumina III-8 7 Glycolic 0.15 Aluminumammoniumethylene- 0.8 Intermediate 1 4 acid diaminetetraacetate Alumina Citric0.05 acid Comp. Ex. No. III-1 7 None — None — None — 4 III-2 7 None —Aluminumammonium 0.8 Intermediate 1 4 ethylene- Aluminadiaminetetraacetate III-3 7 Glycolic 0.15 Aluminumammonium ethylene- 0.8None — 4 acid diaminetetraacetate III-4 7 Glycolic 0.15 None —Intermediate 1 7 acid Alumina III-5 7 None — Diammonium ethylenediamine0.8 Alumina Sol*¹ 1.5 4 tetraacetate*¹Commercially available from Nissan Chemical Industries, Ltd. under thetrade name of Alumina Sol-200.

Using each of the resulting polishing compositions, a substrate surfacemade of an Ni—P plated aluminum alloy, the substrate surface having anaverage deviation, of all points from plane fit to test part surface Raof 0.2 μm, as determined by the method described above, a thickness of0.8 mm and a diameter of 95 mm was polished with a double-sidedprocessing machine under Set Conditions II for Double-Sided ProcessingMachine given above, to give a polished Ni—P plated, aluminum alloysubstrate usable for magnetic recording media.

After polishing, the thickness of the aluminum alloy substrate ofExamples was determined by using a thickness tester (a laser thicknesstester, commercially available from Mitsutoyo Corporation, ModelLGH-110/LHC-11N). A rate of decrease in the thickness was obtained fromthe changes in the thickness of an Ni—P plated aluminum alloy substratebefore and after polishing, and expressed as a relative value (relativepolishing rate) of Comparative Example III-1.

In addition, the surface roughness (average deviation, of all pointsfrom plane fit to test part surface Ra), pits, and roll-off of eachsubstrate after polishing were determined in the same manner inaccordance with the methods described above. Here, the averagedeviation, of all points from plane fit to test part surface Ra wasobtained as a relative value (relative roughness) on the basis of thesurface roughness of Comparative Example III-1. In addition, theroll-off was obtained as a relative value (relative roll-off) on thebasis of the roll-off value of Comparative Example III-2. The resultsare shown in Table 5. TABLE 5 Evaluation of Properties Polishing SurfaceSurface Rate Roughness Defects Roll-Off (−) (−) (Pits) (−) Ex. No. III-12.3 0.70 S 0.26 III-2 2.5 0.75 S 0.28 III-3 2.3 0.67 S 0.30 III-4 2.40.71 S 0.31 III-5 2.3 0.68 S 0.31 III-6 1.8 0.95 A 0.31 III-7 2.0 0.83 S0.42 III-8 2.4 0.74 S 0.25 Comp. Ex. No. III-1 1.0 1.0 C Undeter-minable* III-2 2.2 0.76 S 1.0 III-3 1.8 1.80 B 0.29 III-4 1.4 0.65 S0.28 III-5 1.7 0.92 A 1.05*Undeterminable due to generation of ski jump.

It is clear from the results in Table 5 that all of the polishingcompositions obtained in Examples III-1 to III-8 are excellent,simultaneously satisfying all of effects of increasing polishing rates,effects of reducing surface defects such as pits, effects of reducingsurface roughness and effects of reducing roll-off, as compared withthose of the polishing compositions obtained in Comparative ExamplesIII-1 to III-5.

Further, the polishing composition prepared in each of Example III-5,Example III-8 and Comparative Example III-2 was subjected to polishingevaluation mentioned above for 20 repeated times, and a ratio of atwentieth relative polishing rate to the first relative polishing ratewas determined as a measure for an ability of preventing pad clogging.As a result, the ratio of a twentieth relative polishing rate to thefirst relative polishing rate in the polishing composition of ExampleIII-5 was 0.91, the ratio in the polishing composition of Example III-8was 0.90, and the ratio in the polishing composition of ComparativeExample III-2 was 0.48.

It is clear from the evaluation results of ability of preventing padclogging for the polishing compositions of Examples III-5 and III-8exhibit excellent ability for preventing pad clogging, as compared withthat of Comparative Example III-2.

Examples IV-1 to IV-7 and Comparative Examples IV-1 to IV-3

There were mixed together an abrasive [a-alumina (purity: about 99.9%)having primary average particle size: 0.23 μm, and secondary averageparticle size: 0.6 μm], Compounds (A), Compounds (B), and ion-exchangedwater, and other components as occasion demands, to give a compositionas shown in Table 6 with stirring. Here, the pH of each composition inExamples IV-1 to IV-7 and Comparative Examples IV-2 to IV-3 was adjustedwith nitric acid, and the pH of the composition in Comparative ExampleIV-1 was adjusted with an aqueous ammonia, to a pH of 4.0 or 7.0, togive 100 parts by weight of each polishing composition of Examples IV-1to IV-7 and Comparative Examples IV-1 to IV-3.

Using each of the resulting polishing compositions, a substrate surfacemade of an Ni—P plated aluminum alloy, the substrate surface having anaverage deviation, of all points from plane fit to test part surface Raof 0.2 μm, as determined by the method described above, a thickness of0.8 mm and a diameter of 95 mm was polished with a double-sidedprocessing machine under Set Conditions II for Double-Sided ProcessingMachine given above, to give a polished Ni—P plated, aluminum alloysubstrate usable for magnetic recording media.

After polishing, the thickness of the aluminum alloy substrate ofExamples was determined by using a thickness tester (a laser thicknesstester, commercially available from Mitsutoyo Corporation, ModelLGH-110/LHC-11N). A rate of decrease in the thickness was obtained fromthe changes in the thickness of an Ni—P plated aluminum alloy substratebefore and after polishing, and expressed as a relative value (relativepolishing rate) of Comparative Example IV-1.

In addition, the surface roughness (average deviation, of all pointsfrom plane fit to test part surface Ra) and roll-off of each substrateafter polishing were determined in the same manner in accordance withthe methods described above. Here, the roll-off was obtained as arelative value (relative roll-off) on the basis of the roll-off value ofComparative Example IV-2. The results are shown in Table 6. TABLE 6Compounds (A) Compounds (B) α-Alumina Amount Amount Others Evaluation ofProperties (parts by (parts by (parts by (parts by Polishing weight)Compound weight) Compound weight) weight) pH Rate Roll-Off Ex. No. IV-17 Glycolic 0.15 Aluminumammonium 0.8 — 4 1.9 0.21 acid ethylenediamine-tetraacetate IV-2 7 Glycolic 0.15 Maleic acid 0.5 — 7 2.1 0.22 acid IV-37 Tartaric 0.15 Itaconic acid 0.5 — 7 1.9 0.24 acid IV-4 7 Malonic 0.15Fumaric acid 0.5 — 7 1.9 0.27 acid IV-5 7 Citric 0.15 Diglycolic acid0.5 — 7 2.0 0.24 acid IV-6 7 Glycolic 0.15 Diammonium 0.8 — 4 1.9 0.25acid ethylenediamine- tetraacetate IV-7 7 Glycolic 0.15 Maleic acid 0.5— 7 2.0 0.21 acid Citric 0.05 acid Comparative Examples IV-1 7 None —None — — 4 1 Undeter- minable¹⁾ IV-2 7 None — Aluminumammonium 0.8 — 41.8 1³⁾ ethylenediamine- tetraacetate IV-3 7 None — Succinic acid 0.6Alumina 4 1.5 0.90 Sol²⁾ (0.4)¹⁾Undeterminable due to generation of ski jump.²⁾Commercially available from Nissan Chemical Industries, Ltd. under thetrade name of Alumina Sol-200.³⁾The roll-off value was 0.37 μm/μm.

It is clear from the results in Table 6 that all of the polishingcompositions obtained in Examples IV-1 to IV-7 have high polishingrates, and markedly reduced roll-off in the polished substrate, ascompared with the polishing compositions obtained in ComparativeExamples IV-1 to IV-3.

Further, the polishing composition prepared in each of Example IV-5,Example IV-7 and Comparative Example IV-3 was subjected to polishingevaluation mentioned above for 20 repeated times, and a ratio of atwentieth relative polishing rate to the first relative polishing ratewas determined as a measure for an ability of preventing pad clogging.As a result, the ratio of a twentieth relative polishing rate to thefirst relative polishing rate in the polishing composition of ExampleIV-5 was 0.95, the ratio in the polishing composition of Example IV-7was 0.92, and the ratio in the polishing composition of ComparativeExample IV-3 was 0.55.

It is clear from the evaluation results of ability of preventing padclogging for the polishing compositions of Examples IV-5 and IV-7exhibit excellent ability for preventing pad clogging, as compared withthat of Comparative Example IV-3.

By polishing a substrate for precision parts or the like with theroll-off reducing agent of the present invention, there can be exhibitedexcellent effects that the roll-off of the polished substrate can beremarkably reduced, and that the polishing rate can be increased.

In addition, by polishing a substrate for precision parts or the likewith the polishing composition of the present invention, there can beexhibited excellent effects that the roll-off and the surface roughnessof the polished substrate are remarkably reduced.

Equivalents

The present invention being thus described, it will be obvious that thesame may be varied in many ways. Such variations are not to be regardedas a departure from the spirit and scope of the invention, and all suchmodifications as would be obvious to one skilled in the art are intendedto be included within the scope of the following claims.

1. A polishing composition comprising: water; an abrasive; a roll-offreducing agent comprising one or more compounds selected from the groupconsisting of carboxylic acids having 2 to 20 carbon atoms having eitherOH group or groups or SH group or groups, monocarboxylic acids having 1to 20 carbon atoms, and dicarboxylic acids having 2 to 3 carbon atoms,and salts thereof; and an intermediate alumina.
 2. A polishingcomposition comprising: (A) one or more compounds selected fromcarboxylic acids having 2 to 20 carbon atoms having either OH group orgroups or SH group or groups, monocarboxylic acids having 1 to 20 carbonatoms, and dicarboxylic acids having 2 to 3 carbon atoms, and saltsthereof; (B) one or more compounds selected from polycarboxylic acidshaving 4 or more carbon atoms and having neither OH group or groups norSH group or groups, aminopolycarboxylic acids, amino acids and saltsthereof; and (C) one or more compounds selected from an intermediatealumina and an alumina sol; an abrasive; and water.
 3. The polishingcomposition according claim 2, wherein the intermediate alumina and thealumina sol in Compounds (C) have a specific surface area of from 30 to300 m²/g and an average particle size of 0.01 to 5 μm.
 4. The polishingcomposition according to claim 2, wherein the intermediate alumina isprepared from aluminum hydroxide and/or an alumina sol, each having aspecific surface area of 10 m²/g or more and a content of an alkalimetal and a content of an alkaline earth metal of 0.1% by weight orless.
 5. A polishing composition comprising: (A) one or more compoundsselected from carboxylic acids having 2 to 20 carbon atoms having eitherOH group or groups of SH group or groups, monocarboxylic acids having 1to 20 carbon atoms, and dicarboxylic acids having 2 to 3 carbon atoms,and thereof; and (B) one or more compounds selected from polycarboxylicacids having 4 or more carbon atoms and having neither OH group orgroups nor SH group or groups, aminopolycarboxylic acids, amino acidsand salts thereof; an abrasive; and water.
 6. The polishing compositionaccording to claim 5, wherein one or more compounds of Compounds (A) areselected from carboxylic acids having 2 to 20 carbon atoms having eitherOH group or groups or SH group or groups, and dicarboxylic acids having2 to 3 carbon atoms, and salts thereof, and wherein one or morecompounds of Compounds (B) are selected from polycarboxylic acids having4 or more carbon atoms and having neither OH group or groups nor SHgroup or groups, aminopolycarboxylic acids, and salts thereof.
 7. Thepolishing composition according to claim 5, wherein one or morecompounds of Compounds (A) are selected from oxalic acid, malonic acid,glycolic acid, lactic acid, malic acid, glyoxylic acid, tartaric acid,citric acid, gluconic acid, and salts thereof, and wherein one ore morecompounds of Compounds (B) are selected from succinic acid, maleic acid,fumaric acid, citraconic acid, itaconic acid, tricarballylic acid,diglycolic acid, ethylenediaminetetraacetic acid,diethylenetriaminepentaacetic acid, and salts thereof.
 8. A polishingprocess of a substrate to be polished comprising a step of polishing thesubstrate to be polished with the polishing composition of any one ofclaims 1 to 7.